1、技術原理：Art of Technology:

采用納米氧化鋁為原料，集材料科學、凝聚態物理、表面、界面等多學科綜合技術，經高度濃縮懸浮生產工藝，通過納米顆粒表面修飾技術、凝膠澆注成型技術等制備出的高強度、耐高溫的泡沫陶瓷。本產品使用高溫度可以達到1750℃，是我國目前硅酸鋁、多晶莫來石、氧化鋁纖維等輕質材料無法達到的。

The  Alumina Oxide Ceramic Foam Insulation  was manufactured based on the  multiple technologies of Material Science, Condensed Matter Physics, Surface/ Interface science with the Nano Particle of Alumina oxide . With the art of technology of highly concentrated suspension process, surface modification of nano-particles and Sol-Gel casting,the Alumina oxide ceramic foam with excellent compressive and flexural strength was developed. The application temperature can be high as 1750⁰C which is not available for aluminium silicate, polycrystal mullite ,alumina based ceramic fiber or any other light weight brick in the market.

2、技術特點：Characteristics:

（1）純度高，氧化鋁含量高于95%。

High Purity: Al2O3 > 95%;

（2）使用溫度高，可達到1750℃。

Application temperature: up to 1750℃

（3）強度高，相比耐火纖維使用壽命大大提高。

High strength: much longer lift time than RCF.

（4）體積密度低，為0.2-0.5 g/cm3 。

Ultra-low density: 0.2-0.5 g/cm³

（5）熱導率、線性膨脹系數低。

Low Thermal Conductivity and Linear Thermal expansion coefficient;

（6）“Fiber-Free”，生產和使用過程中對人體無害。

Fiber free: harmless to people in the production and using process.

（7）耐沖擊，可以快速加熱和冷卻。

Great Thermal Shock Resistance: can be used for quickly heating and cooling. 

3、技術指標：Specifications:

4、應用領域：Applications:

（1）1000-1750度實驗室及工業爐爐襯。

1000ºC-1750ºC laboratory or industrial furnace lining;

（2）電熱或者燃氣爐爐襯。

Electric or gas heating furnace lining;

（3）臺車爐爐襯。Kiln cars lining;

（4）使用溫度需要達到1750ºC的應用。

All applications when temperature achieved 1750ºC;

（5）含有H2 & CO的還原氣氛或者氧化氣氛的高溫領域;

High temperature field with H₂, CO or other reducing / oxidizing atmosphere.